X53-4 Highly Chlorinated Polyethylene Anti-corrosive Paint With Micaceous Iron Oxide

X53-4 Highly Chlorinated Polyethylene Anti-corrosive Paint With Micaceous Iron Oxide

Intended Uses Suited for protecting surface of all steel installatins subject to chemically and industrially atmospheric corrosion as primer as well as surface of concrete installations. It forms an excellent anti-corrosive coating with good resistance to water, tough film, high adhesion, quick dry owing to flake micaceous iron oxide is oriental and parallel arrangement and overlappin each other as fish scale, besides other functions of the pigments.
Product Description Red brown or grey.
Product Information Volume Solids 35-38%
Dry Film Thickness 45-50microns equivalent to 125-140 microns of wet film.
Theoretical Coverage 185-196g/m2
Pratical Coverage Allow appropriate loss
Application Details Mix Ratio One package
Method of Application
Airless Spray Recommended-Tip range 0.43-0.53mm, Total output fluid pressure: 17.3MPa(176Kg/sq.cm)
Brush or Roller Recommended
Conventional Spray No recommended
Thinner X-27
Cleaner X-27
Pot Life No limit
Storage Life One year
Drying
Time
Substrate
Temperature
Touch
Dry
(h)
Hard
Dry
(h)
Overcoating Interval
Minimum Maximum
0℃
25℃
30℃
1 24

24 hours
8 hours
6 hours

7 days
7 days
7 days
Storage and Handing Storage Store in cool and dry conditions
Pack Size 25kg in 20 liter container
Flash Point 38℃
Specific Gravity Approx 1.38kg/L
Specification and Surface Preparation Steel surface: clean to Swedish Sa2.5 or rust-removed manually or with power to tool to Swedish Standard St3.
Safety Precautions This product should be used in painting area by professional operations. When painting, please refer to Product Data Sheet and MSDS. Consult our company if consumers could not completely understand the precautions for safety and health when applying this product.
This product is a kind of solvent-based paint. In order to avoid danger or accident, minimal safety precautions, as follow, should be done;
The paint contains volatile solvent and is flammable. So must keep away form sparks and open flames. No smoking at application site. Effective precautions (such as using explosion-proof electrical equipments, no static electricity accumulation or metal collision etc) also should be done so as to avoid producing sparks. Flash point of paint, mentioned above o Product Data Sheet, is the lowest temperature at which mixture of the volatile materials of paint can ignite or explode with air.
Enough ventilation is necessary at application site. In order to remove any danger of explosion, must keep the ratio of gas to air is less than 10%, the minimum explosive limit in general. Therefore, 200m3 of ventilation quantity per 1kg solvent (according to the solvent) is necessary.
Protect skin and eyes, and avoid touching with paints (Recommend to wear working clothes, gloves, eye protection, face masks, barries creams and so on). If paint gets in touch with skin, wash fully with a large amount of fresh water and soap or appropriate commercial cleaner. In case of eyes being contaminated, rinse with fresh water for 10min at least and give medical treatment immediately.
Recommend face guard with ventilation pipe for the sake of no absorption of paint fog and harmful solvent gas, especially in bad ventilation. Handle empty containers with care and do not bring about environmental contamination.
NOTICE: If consumers have not taken effective safety precautions (Refer to the specifications), out company will NOT be responsiblefor any accident.