LMF53-1 Chlorine Ether Iron Oxide Red Anti-rust Paint

LMF53-1 Chlorine Ether Iron Oxide Red Anti-rust Paint

Intended Uses It's coating adhesive force is excellent, with good waterproof and chemical anticorrosive performances. This pain does not contain saponifiable ester bond, and has waterproof and chemical anticorrosive performances due to very stable helium atorn combined. Without reactive double bond, it is not easy to degrade by atmosphetie oxygenation, coating resistances to atmospheric aging, with excellent light resistance stability, and it will not yellow or pulverizate. Vinyl isobutyl ether saponificated by copolymer of vinyl chloride and vinyl isobutyl ether has inner plasticity, the coating has enough supplenes without foreign plasticizer, it will not be brittleness because of migration and loss of plasticizer. It contains copolymerizating vinyl chloride ether, so it can guarantee that the paint has excellent adhesive force on various basic materials like surfaces of aluminum and zincoid. It is applicable to heavy anti-corrosion required by steel structure of ship and bridge, and it also can be used as anti-rust primer of galvanized steel plate.
Product Description It is two-component paint consisting of chlorine ether resin, special modified resin, pigments and fillers, auxiliaries, solvent and curing agent. (Iron red)
Product Information Volume Solids 45%
Dry Film Thickness 30 microns
Theoretical Coverage 95g/m2(calculated by 30μm dry film)
Application Details Mix Ratio Component A : Component B =100:6(weight ratio)
Curing Time 23±2℃:0.5-1h
Method of Application
Airless Spray Recommended-Tip range: 17-21mm; Total fluid pressure: 15-20 Mpa
Brush or Roller Recommended, only for small area.
Conventional Spray Adoptable but thin to 5-10%, Tip range:2-2.5mm
Thinner LMP53-1 Special diluent
Pot Life 25℃:8h
Storage Life One year
Drying
Time
Substrate
Temperature
Touch
Dry
(h)
Hard
Dry
(h)
Full Solidification
(d)
Overcoating Interval
Minimum Maximum
25℃ 1 24 7 1 hour No limit
Storage and Handing Storage Store in cool and dry conditions
Pack Size Component A 20kg, Component B 1.2kg.
Specific Gravity Approx 1.33kg/L
Specification and Surface Preparation Painted surface must be cleaned throughly before construction, painted surface shall have no corrosion, water stains or dust, etc. new steel structual surface and steel structural maintenance of general anticorroive engineering can use manual de-rusting or manual mechanical de-rusting to reach derusting standard Grade St3, important anticorrosive engineering and new steel structual surface de-rusting is best to adopt sand blasting or acid picking to remove rust, sand blasting de-rusting reaches Grade Sa2 or Grade Sa2.5, acid picking de-rusting reaches Grade Be. Roughness on blasting surface shall be controlled approx 40μm, basic material surface shall be neutral after acid picking and passivation, the primer shall be painted within 12h after moving rust tu avoid the secondary rusting.
Limitations Substrate temperature must be 3℃ higher than dew point above, and relative humidity must be less than 85%.
Safety Precautions This product should be used in painting area by professional operations. When painting, please refer to Product Data Sheet and MSDS. Consult our company if consumers could not completely understand the precautions for safety and health when applying this product.
This product is a kind of solvent-based paint. In order to avoid danger or accident, minimal safety precautions, as follow, should be done;
The paint contains volatile solvent and is flammable. So must keep away form sparks and open flames. No smoking at application site. Effective precautions (such as using explosion-proof electrical equipments, no static electricity accumulation or metal collision etc) also should be done so as to avoid producing sparks. Flash point of paint, mentioned above o Product Data Sheet, is the lowest temperature at which mixture of the volatile materials of paint can ignite or explode with air.
Enough ventilation is necessary at application site. In order to remove any danger of explosion, must keep the ratio of gas to air is less than 10%, the minimum explosive limit in general. Therefore, 200m3 of ventilation quantity per 1kg solvent (according to the solvent) is necessary.
Protect skin and eyes, and avoid touching with paints (Recommend to wear working clothes, gloves, eye protection, face masks, barries creams and so on). If paint gets in touch with skin, wash fully with a large amount of fresh water and soap or appropriate commercial cleaner. In case of eyes being contaminated, rinse with fresh water for 10min at least and give medical treatment immediately.
Recommend face guard with ventilation pipe for the sake of no absorption of paint fog and harmful solvent gas, especially in bad ventilation. Handle empty containers with care and do not bring about environmental contamination.
NOTICE: If consumers have not taken effective safety precautions (Refer to the specifications), out company will NOT be responsiblefor any accident.